Oxidized asphalt 105/15
Description of oxidized asphalt 105/15
Oxidized asphalt 105/15 (another word, blown asphalt 105/15, oxidized bitumen 105/15) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized asphalt 105/15 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.
RABIT Company guaranty the quality of RABIT Oxidized asphalt 105/15 with the arrangement of the international inspector to check quality and quantity of the Oxiasphalt 105/15 during the loading to the vessel and controlling the production by QC by batch test report before shipping. RABIT Company guarantees the quality to meet with ASTM.
Uses of oxidized asphalt 105/15
Oxidized asphalt 105/15 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The oxidized asphalt 105/15 products are for paving. also used in asphalt-based paints for corrosion protection of metals, in lining public works structures, adhesives in electrical laminates, base for synthetic turf; typical uses for asphalt 105/15 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Asphalt 105/15 is using insulation and isolation bitumen membrane sheet. Car undercoating Automobile industry is specially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof and noise proof for automobile undercoating.
Application of oxidized asphalt 105/15
The oxidized asphalt 105/15 should be heated double temperature against the softening point to support have flow and viscosity. To use asphalt 105/15, surfaces must be dry, clean and after loose particles, formwork, curing products, irregularities, slurry, etc.
Storage/handling of oxidized asphalt 105/15
Oxiasphalt 105/15 has 10 years validity with multi-time heating and cooling, please refer to MSDS.
Packing of oxidized bitumen 105/15
Various pickings are available for customer’s purpose and conveniences. RABIT CO is the manufacturer of asphalt 105/15 in various packing including Kraft bag, meltable plastic bag, drum, and bulk oxidized asphalt 105/15 from penetration grade bitumen.
RABIT asphalt 105/15 perchance supplied in any grade and are designated by two numbers to indicate the softening point and penetration ranges. The oxidized asphalt grade 105/15 means the softening point is 105 and penetration are 15 desi millimeters is produced in compliance and conformity with ASTM standard and meets the following specification.
Specification of oxidized bitumen 105/15
Analysis oxidized bitumen 105/15
| Bitumen 105/15 | Test method | Unit | Specification |
| Specific gravity @25/25 C | ASTM D70 | (Kg/m3) | 1.05 approx. |
| Penetration @ 25°c | ASTM D5 | mm/10 | 10/20 |
| Softening point °c | ASTM D36 | °C | 100/110 |
| Loss on heating(wt) % | ASTM D6 | Wt. % | 0.2 max |
| Flashpoint c | ASTM D92 | °C | 250 min |
| Solubility is CS2(wt) % | ASTM D4 | Wt. % | 99.5 max |
| Spot test | A.A.S.H.O.T102 | — | Negative |